We describe herein the synthesis and characterization of the complexes KNiF3, [Ni(en)3]I2, [Ni(en)3]Cl2, [Ni(acac)2(H2O)2], [Ni(en)2(H2O)2]Cl2 and [Ni(NH3)6](BF4)2 (en = ethylenediamine, acac- = acetylacetonate) performed in the inorganic synthesis major course at the Chemistry Institute of UFRGS (Universidade Federal do Rio Grande do Sul). The compounds were characterized by infrared and electronic spectroscopy and the electrolytic conductivity was measured. The parameters 10Dq and B were obtained from the electronic spectra and the nefelauxetic and spectrochemical series were determined. The obtained spectrochemical series was F- < acac- < NH3 < en and the nefeulaxetic series was en < NH3 < acac- < F-.

Nanocompósitos de polietileno-MMT foram preparados através da metodologia de polimerização in situ utilizando TpMs*TiCl3 (1) intercalado na galeria da Cloisite® 30B (C30B) e na presença de metilaluminoxano (MAO) como ativador. Através da análise de difração de raios-X (DRX) foi observado que o espaçamento basal da argila ativada muda de 1,85 nm (2θ = 4,8) para 2,18 nm (2θ = 4,0) indicando a ocorrência da intercalação do catalisador de titânio na galeria da argila. O sistema catalítico 1/C30B/MAO foi ativo na polimerização do etileno sob diferentes condições reacionais. A morfologia esfoliada do nanocompósito PE-MMT foi confirmada pela análise de difração de raios-X (DRX) e microscopia eletrônica de transmissão (MET). A presença de argila esfoliada (5% em peso) na matriz polimérica confere melhores propriedades mecânicas (módulo de flexão e módulo de armazenamento) quando comparada com aquelas apresentadas pelo polietileno puro produzido exclusivamente por 1.

Polyethylene-MMT nanocomposites were prepared by in situ polymerization methodology using TpMs*TiCl3 (1) intercalated into the gallery of Cloisite® 30B (C30B) using methylaluminoxane (MAO) as activator. From the powder X-ray diffraction (XRD) analysis it was observed that the basal spacing of the activated organoclay changes from 1.85 nm (2θ = 4.8) to 2.18 nm (2θ = 4.0) indicating that the intercalation of the titanium catalyst into the gallery took place. The catalytic system 1/C30B/MAO was active in the ethylene polymerization under different reaction conditions. The exfoliated morphology of the PE-MMT nanocomposite was further examined and confirmed by X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis. The presence of exfoliated clay (5 wt.%) in the PE matrix confers better mechanical properties (flexural modulus and storage modulus) when compared with the ones displayed by the neat PE produced using exclusively 1.